  • Item
    Element Birth and Death Method Application to Lamellar Crack Analysis
    (Wydawnictwo Politechniki Łódzkiej ; Katedra Dynamiki Maszyn - Wydział Mechaniczny Politechniki Łódzkiej, 2015) Jaroniek, Mieczysław; Niezgodziński, Tadeusz
    Load structure, the maximum permissible load is usually determined by the strength calculation (bearing data. Yield stress or strength of the material), or the parameters of fracture mechanics. The paper analyzes the calculations lamellar cracks formed in the lower crane girders steel belts. These cracks are formed in rolled sheets of non-metallic inclusions. The determination of the cracks in the existing designs are extremely difficult. It requires testing metallographic, ultrasonic or acoustic methods. Based on typical images of metallographic steel plates specified place of occurrence of cracks lamellar and sampling, and has subsequently been adopted for the calculation of numerical models of material structure and distribution of artificial joints. In order to analyze the propagation of cracks and formation of lamellar phase slots and destruction was carried out modeling studies and numerical methods cracking process.
  • Item
    Propagation of the Lamellar Cracks.
    (Lodz University of Technology. Faculty of Mechanical Engineering. Department Division of Dynamics., 2014) Jaroniek, Mieczysław; Niezgodziński, Tadeusz
    The aim of the study is to include studying the effects of the interaction of lamellar cracks and their effect on the degradation of the structure. Lamellar cracking phenomenon is most common in the construction of welded ship hulls, bridges, pressure vessels and piping. The structures of these, as a result of errors in production and welding cracks. The sudden breakage occurs in the construction of real time, although they have been designed properly in terms of both the volume of the stress and strain. The growth of these cracks, at a rate equal to the speed of sound in the material, it is a sudden breakage.
  • Item
    Study of the Formation of Lamellar Cracks.
    (Lodz University of Technology. Faculty of Mechanical Engineering. Department Division of Dynamics., 2014) Jaroniek, Mieczysław; Niezgodziński, Tadeusz
    In rolled sheets, non-metallic inclusions are distributed along the thickness of the sheet as narrow lines running parallel to the rolling direction. Such inclusions are the nuclei of lamellar cracks. This work presents the application of the numerical method for study of lamellar cracking. Numerical models of samples with long artificial fissures set in the area of the sheet axis were studied along with other encountered inclusion distributions. Changes in the stress state in the area of the inclusion were observed as the load increased. Stress concentration leads to the formation of lamellar cracks - the joining of voids in the direction parallel to the exterior surface of the sheet (so-called "terraces" are formed) and at angles (so-called "jogs" are formed). The results of experimental tests were compared with the results of numerical calculations using the finite element method.
  • Item
    Element Birth and Death Method Application to Lamellar Crack Analysis.
    (Lodz University of Technology. Faculty of Mechanical Engineering. Department Division of Dynamics., 2015) Jaroniek, Mieczysław; Niezgodziński, Tadeusz
    Load structure, the maximum permissible load is usually determined by the strength calculation (bearing data. Yield stress or strength of the material), or the parameters of fracture mechanics. The paper analyzes the calculations lamellar cracks formed in the lower crane girders steel belts. These cracks are formed in rolled sheets of non–metallic inclusions. The determination of the cracks in the existing designs are extremely difficult. It requires testing metallographic, ultrasonic or acoustic methods. Based on typical images of metallographic steel plates specified place of occurrence of cracks lamellar and sampling, and has subsequently been adopted for the calculation of numerical models of material structure and distribution of artificial joints. In order to analyze the propagation of cracks and formation of lamellar phase slots and destruction was carried out modeling studies and numerical methods cracking process.